PolyWood is a pre-foamed wood-mimic printing material that contains no actual wood, ensuring a clean, Jam-Free printing experience
PolyWood 1.75mm 600g
$57.00
説明
Brand：Polymaker
Wood with no mess
Instead of using wood to mimic wood, we developed a unique foaming technology PolyWood is composed entirely of polymers, The Results?Excellent print quality and jam-free printing
Light Weight
The density PolyWood is so light,0.8g/m³ to be exact, it is 35%lighter than regular PLA, This leads to many interesting properties and potential applications
Endless Possibilities
Since PolyWood contains no actual wood, we can create any colour aesthetic we want, As it also contains a foamed structure, parts printed in PolyWood can achieve amazing surface finish
Jam-Free
Out patented Jam-Free technology dramatically improves the heat stability of PLA filaments by raising the softening temperature ensuring a worry free printing experience
Uncompromised Quality
With our eight step quality control process and rigorous in-house testing, you can rest assured that PolyFlex will produce beautiful, reliable and accurate printed parts every time
Physical Properties
| Property | Testing Method | Typical Value |
|---|---|---|
| Density(g/m³ at 21.5°C | Custom method | ~0.8 |
| Melt index(g/10min) | —— | Not available |
Mechanical Properties
| Property | Testing Method | Typical Value |
|---|---|---|
| Tensile strength(MPa) | ASTM D638(ISO 527,GB/T 1040) | 23.2±0.4 |
| Elongation At Break(%) | ASTM D638(ISO 527,GB/T 1040) | 8.21±0.87 |
| Bending strength(Mpa) | ASTM D790(ISO 178,GB/T 9341) | 52.9±0.30 |
| Impact strength(KJ/m² | ASTM D256(ISO 179,GB/T 1043) | 2.06±0.19 |
Testing Geometries
追加情報
| Density | ~0.8g/m³ |
|---|---|
| Melt Flow Index(g/10min) | Not available |
| Tensile Strength | 23.2±0.4Mpa |
| Elongation At Break | 8.21±0.87% |
| Bendling Strength | 1.36±0.30Mpa |
| IZODImpact Strength | 2.06±0.19kj/m² |